Virgin PC Plastic Granules Pellets PC Raw Material Polycarbonate Resin

• Customization: Available
• Feature: High Transparency
• CAS No.: 25037-45-0
• Formula: (C15h16o2. CH2o3)X
• EINECS: 200-815-3
• Material: Polycarbonates/PC
• Usage: Engineering Plastics
• Plastic Forming Method: Extrusion
• Color: Transparent
• Product Name: Virgin Polycarbonate(PC) Resin
• Keywords: Polycarbonate Resin Granules
• Type: Resins PC Pellets
• MOQ: 5kg
• Package: 25kg/Bag
• Application: Lens
• Grade: Extrusion Grade, Injection Molding Grade
• Transport Package: 25kg/Bag
• Specification: Pellet / Granules / Polymer
• Trademark: Julier
• Origin: China
• HS Code: 3907400010
• Production Capacity: 1000000kgs

Product Description

Product Description

 

pc is an almost colorless glassy amorphous polymer with good optical properties. PC high molecular weight resin has high toughness. The notched Izod impact strength of the cantilever is 600 ~ 900J / m, and the heat distortion temperature of the unfilled grade is about 130 ° C. This value can be increased by 10 ° C after glass fiber reinforcement. The flexural modulus of PC can reach more than 2400MPa, and the resin can be processed into large rigid products. Below 100 ° C, the creep rate under load is very low. PC has poor hydrolysis resistance and cannot be used in products that are repeatedly subjected to high pressure steam. The main performance defects of PC are insufficient hydrolysis resistance, sensitivity to notches, resistance to organic chemicals, poor scratch resistance, and yellowing after long-term exposure to ultraviolet light. Like other resins, PCs are susceptible to attack by certain organic solvents. pc gf 20 material is flame retardant. Antioxidant. Polycarbonate is colorless and transparent, heat-resistant, impact-resistant, flame-retardant BI grade, and has good mechanical properties at ordinary use temperatures. Compared with performance close to polymethyl methacrylate, polycarbonate has good impact resistance, high refractive index, and good processing performance. It does not require additives to have UL94 V-2 flame retardancy. However, polymethyl methacrylate is cheaper than polycarbonate, and large-scale devices can be produced by bulk polymerization.

 

 

Performance Item	Test Conditions	Test Method	Test Data	Data Unit
Melt flow rate	---	ASTM D-1238	10-15	g/10min
Density	---	ASTM D-792	1.2	G/cc
Shrinkage	---	ASTM D-955	0.005-0.007	mm/mm
Transparency	---	ASTM D-1003	80-85	%
Notched Cantilever Impact Strength	---	ASTM D-256	45	KJ/m^2
Tensile Strength at break	---	ASTM D-638	65	MPa
Flexural Strength	---	ASTM D-638	80	MPa
Flexural Modulus	---	ASTM D-790	2.37	GPa
Elongation at Break	---	ASTM D-638	90	%
Heat deformation Temperature	0.45MPa	ASTM D-648	130	ºC
Flammability	1.5mm	UL 94	HB	---

 

Company Profile

Julier has been one of the leading forces within the plastic materials industry since it was founded in 2003. Julier engaged in compound plastics and engineering plastics, such as PA6, PA66, PA12, PC, PBT, ABS, TPU, PEI, PSU, POM, PC+ABS, etc. which can be reinforced with glass fiber reinforced, flame retardant, carbon fiber, Mos2, toughness, etc. The most important thing is we have an R&D department, so we can customize products and provide technical support according to customers' needs. To be your best plastic profile manufacturer, we're striving to provide you with good quality products and services and offer moderate prices as we realize that the profitability is the number one goal of our valued customers.